Effect of preparation design on fracture strength of compromised molars restored with lithium disilicate inlay and overlay restorations: An in vitro and in silico study.

PURPOSE

The objective of this study was to determine the influence of different preparation designs on the fracture strength, failure type, repairability, formation of polymerization-induced cracks, and tooth deformation of structurally compromised molars restored with lithium disilicate inlays and overlays in combination with Immediate Dentin Sealing (IDS).

MATERIAL AND METHODS

Human molars (N = 64) were randomly assigned to four different preparation designs: Undermined Inlay (UI), Extended Inlay (EI), Restricted Overlay (RO), and Extended Overlay (EO). The teeth were restored using lithium disilicate partial restorations and subjected to thermomechanical fatigue in a chewing simulator (1,2 × 10 (Mondelli et al., 2007) cycles on 50 N, 8000x 5-55 °C), followed by load to failure testing. In silico finite element analysis was conducted to assess tooth deformation. Polymerization-induced cracks were evaluated using optical microscopy and transillumination. Fracture strengths were statistically analyzed using a Kruskal-Wallis test, while the failure mode, repairability, and polymerization cracks were analyzed using Fisher exact test.

RESULTS

The propagation of polymerization-induced cracks did not significantly differ among preparation designs. All specimens withstood chewing simulator fatigue, with no visible cracks in teeth or restorations. Fracture strength was significantly influenced by preparation design, with restricted overlay (RO) showing higher fracture strength compared to extended inlay (EI) (p = .042). Tooth deformation and fracture resistance correlated between in vitro and in silico analyses). UI exhibited a statistically less destructive failure pattern than EO (p < .01) and RO (p = .036). No statistically significant influence of the preparation design on repairability was observed. Groups with higher repairability rates experienced increased tooth deformation, leading to less catastrophic failures.

CONCLUSIONS

The preparation design affected the fracture strength of compromised molars restored with lithium disilicate inlays and overlays, with significantly lower fracture strength for an extended inlay. The failure pattern of lithium disilicate overlays is significantly more destructive than that of undermined and extended inlays. The finite element analysis showed more tooth deformation in the inlay restorations, with lower forces in the roots, leading to less destructive fractures. Since cusp coverage restorations fracture in a more destructive manner, this study suggests the undermined inlay preparation design as a viable option for restoring weakened cusps.