A high-temperature and high-pressure flow-reactor system was applied to the synthesis of monometallic ruthenium (Ru) nanoparticles and platinum/ruthenium (Pt/Ru) bimetallic nanoparticles using the thermal reduction of ruthenium ion (Ru(III)) and the mixture of platinum (Pt(IV)) and ruthenium ions in water and ethanol mixture in the presence of poly(N-vinyl-2-pyrrolidone). Monometallic Ru nanoparticles with an average diameter of ca. 2 nm were synthesized above 200 degrees C at 30 MPa. The monometallic Ru nanoparticles tended to make large aggregates in colloidal dispersions. By the reduction of the mixture solution of Pt(IV) and Ru(III) in water and ethanol above 200 degrees C at 30 MPa, Pt/Ru bimetallic nanoparticles with an average diameter of ca. 2.5 nm were synthesized with relatively small size distribution. The EXAFS spectra for the Pt/Ru bimetallic particles indicated that the particle possesses metallic bonds between Pt and Ru atoms in contrast to the case of the nanoparticles produced by thermal reduction under ambient pressure at 100 degrees C [M. Harada, N. Toshima, K. Yoshida, S. Isoda, J. Colloid Interface Sci. 283 (2005) 64], and that the Pt/Ru bimetallic particle has a Pt-core/Ru-shell structure.