Piddock V, Qualtrough A J, Slevin A, Fernandes J C
Department of Restorative Dentistry, University of Manchester Dental Hospital, England.
Int J Prosthodont. 1995 May-Jun;8(3):280-4.
The effects of experimental lithium-containing ion exchange pastes on dental porcelain were compared with a commercial ion strengthening paste. Maximum biaxial flexure strength using the experimental pastes was obtained by firing lithium paste containing 200 g per L lithium sulphate dihydrate for 45 minutes at 750 degrees C onto the surface of the porcelain. However, the commercial paste produced the greatest strengthening overall.
将实验性含锂离子交换糊剂对牙科瓷器的影响与一种商业离子强化糊剂进行了比较。使用实验性糊剂获得的最大双轴弯曲强度是通过在750摄氏度下将含有每升200克二水合硫酸锂的锂糊剂烧制45分钟到瓷器表面上得到的。然而，商业糊剂总体上产生了最大的强化效果。