Yang Y, Kim K-H, Agrawal C M, Ong J L
The University of Texas Health Science Center at San Antonio, Department of Restorative Dentistry, Division of Biomaterials, MSC 7890, 7703 Floyd Curl Drive, San Antonio, TX 78229-3900, USA.
J Dent Res. 2003 Oct;82(10):833-7. doi: 10.1177/154405910308201014.
Extensive research suggested that calcium phosphate (CaP) coatings on titanium implants are essential for early bone response. However, the characterization of CaP crystallinity and the means to control coating crystallinity are not well-established. In this study, the effect of a 400 degrees C heat treatment for 1, 2, or 4 hours, and in the presence or absence of water vapor, on CaP crystallinity was investigated. Scanning electron microscopy indicated dense as-sputtered coatings. Increase in coating crystallinity was observed to be consistent with the increasing number of PO(4) peaks observed as a result of different heat treatments. In addition, x-ray diffraction analyses indicated amorphous as-sputtered coatings, whereas crystalline CaP coatings in the range of 0-85% were observed after different post-deposition heat treatments. It was concluded that the presence of water vapor and post-deposition heat treatment time significantly affect the crystallinity of CaP coatings, which may ultimately affect bone healing.