Quantification of the disorder in network-modified silicate glasses.

Local order in silicate glasses has been observed by many experimental techniques to be similar to that in crystalline materials. Details of the intermediate-range order are more elusive, but essential for understanding the lack of long-range symmetry in glasses and the effect of composition on glass structure. Two-dimensional 17O dynamic-angle-spinning nuclear magnetic resonance experiments reveal intermediate-range order in the distribution of inter-tetrahedral (Si-O-Si) bond angles and a high degree of order in the disposition of oxygen atoms around the network-modifying cations.