Dymek S, Wróbel M, Blicharski M
AGH University of Science and Technology, 30-059 Kraków, Al. Mickiewicza 30, Poland.
J Microsc. 2006 Sep;223(Pt 3):292-4. doi: 10.1111/j.1365-2818.2006.01658.x.
This article presents preliminary results of the processing and characterization of gamma-TiAl alloy modified by W addition. An alloy with the target chemical composition of TiAl-5W (at.%) was synthesized by mechanical alloying. Two methods were used for powder compaction: hot pressing at 1300 degrees C and hot extrusion at 1100 degrees C. Hot extrusion turned out to be a superior consolidation technique over hot pressing. The matrix of final alloy was composed of a phase based on TiAl and a minor amount of Ti(3)Al. The grain size in the extruded alloy was much smaller than in the hot-pressed one. Minute W particles formed a dispersoid.