The objective of this manuscript is to outline the relationship between bond strength tests of adhesive materials and other in vitro phenomena by reviewing the literature generated over the thirty years.
Information was gathered from nearly 30 published articles appearing in dental literature. Studies were predominantly identified through a search of the PubMED database with a few additional studies published in Japanese domestic journals.
Studies were included that provided evidence for the relationship between results of evaluations of the bond strengths and other in vitro phenomena such as micro-leakage, nanoleakage, structural of bonding interface and mechanical properties of bonding interface. An attempt was made to select articles that spanned the timeframe from approximately 1980 to today to try to ensure that the classic literature as well as the latest information was included.
Previous studies have indicated bond strength did not correlate with the results of micro-leakage tests nor gap formation at the cavity margin. The nanoleakage test and morphological and chemical characteristics of the bonding interface had potential to predict the dentin bond durability.
Bond strength test results and other in vitro phenomena was not evenly correlated. According to the development of the materials, the most appropriate bond test and analysis of the in vitro phenomena should be also developed.
通过回顾三十年来的文献，概述粘接材料的粘接强度测试与其他体外现象之间的关系。
从近 30 篇发表在牙科文献中的已发表文章中收集信息。研究主要通过在 Pubmed 数据库中搜索发现，同时也有一些在日本国内期刊上发表的额外研究。
纳入了提供粘接强度评估结果与其他体外现象（如微渗漏、纳米渗漏、粘接界面结构和粘接界面力学性能）之间关系证据的研究。尝试选择涵盖大约从 1980 年到今天的时间段的文章，以确保包括经典文献和最新信息。
以前的研究表明，粘接强度与微渗漏测试结果或腔缘处的间隙形成无关。纳米渗漏测试以及粘接界面的形态和化学特征有可能预测牙本质粘接耐久性。
粘接强度测试结果与其他体外现象并非均匀相关。根据材料的发展，也应开发出最适合的粘接测试和体外现象分析。