Optical characterization of Eu3+ and Tb3+ ions doped cadmium lithium alumino fluoro boro tellurite glasses.

This article reports on the development and spectral results of Eu(3+) and Tb(3+) ions doped cadmium lithium alumino fluoro boro tellurite (CLiAFBT) glasses in the following composition. 40TeO2-30B2O3-10CdO-10Li2O-10AlF3 (Hostglass) (40-x)TeO2-30B2O3-10CdO-10Li2O-10AlF3-xEu2O3 (40-x)TeO2-30B2O3-10CdO-10Li2O-10AlF3-xTb4O7 where x=0.25, 0.50, 0.75, 1.0, 1.25 mol%. Glass amorphous nature and thermal properties have been studied using the XRD and DSC profiles. From the emission spectra of Eu(3+):glasses, five emission transitions have been observed at 578 nm, 592 nm, 612 nm, 653 nm, 701 nm and are assigned to the transitions (5)D(0)→(7)F(0), (7)F(1,)(7)F(2), (7)F(3) and (7)F(4), respectively, with λ(exci)=392 nm ((7)F(0)→(5)L(6)). In case of Tb(3+):glasses, four emission transitions ((5)D(4)→(7)F(6,)(7)F(5), (7)F(4) and (7)F(3)) are observed at 488 nm, 543 nm, 584 nm and 614 nm, respectively, with λ(exci)=376 nm. Decay curves and energy level diagrams have been plotted to evaluate the life times and to analyze the emission mechanism.