Chem Commun (Camb). 2011 May 28;47(20):5876-8. doi: 10.1039/c1cc10894h. Epub 2011 Apr 14.
We demonstrate an alternative route to tune the morphology of zeolite L crystals using C(2)H(5)OH as the co-solvent in the synthesis gel. A low aspect ratio (0.2 to 0.4) of zeolite L crystals was obtained at lower synthesis temperature (150 °C) and shorter synthesis duration (3 days).
我们展示了一种通过使用 C(2)H(5)OH 作为共溶剂来调整沸石 L 晶体形貌的替代途径。在较低的合成温度（150°C）和较短的合成时间（3 天）下，获得了低纵横比（0.2 至 0.4）的沸石 L 晶体。