Optical, thermal and dielectric properties of Sr(II)-doped bis(thiourea)zinc(II) chloride crystals.

The influence of strontium doping on the properties of bis(thiourea)zinc(II) chloride (BTZC) crystals has been described. The reduction in the intensity observed in powder X-ray diffraction of doped specimen and slight shifts in vibrational frequencies confirm the lattice stress as a result of doping. The incorporation of Sr(II) into the crystal lattice was confirmed by energy dispersive X-ray spectroscopy (EDS). Surface morphological changes due to doping of the alkaline earth metal are observed by scanning electron microscopy (SEM). The crystal is transparent in the entire visible region having a lower optical cut-off at ~308 nm with a band gap energy of 4.06 eV. The DSC studies reveal the purity of the materials and no decomposition is observed up to the melting point. Dielectric studies show that the isovalent ion Sr(II)-doping altered the dielectric properties of the host crystal.