The influence of resin cements on the final color of ceramic veneers.

作者信息

Chen Xiao-Dong, Hong Guang, Xing Wen-Zhong, Wang Yi-Ning

机构信息

The State Key Laboratory Breeding Base of Basic Science of Stomatology (Hubei-MOST) & Key Laboratory of Oral Biomedicine Ministry of Education, School & Hospital of Stomatology, Wuhan University, Wuhan, China; Department of Prosthetics, Dalian Stomatological Hospital, Dalian, China.

Liaison Center for Innovative Dentistry, Graduate School of Dentistry, Tohoku University, Sendai, Japan.

出版信息

J Prosthodont Res. 2015 Jul;59(3):172-7. doi: 10.1016/j.jpor.2015.03.001. Epub 2015 Apr 1.

DOI:10.1016/j.jpor.2015.03.001

PMID:25840891

Abstract

PURPOSE

To evaluate the effect of three brands of resin cement on the final color of ceramic veneers.

METHODS

50 disk-shaped ceramic specimens (IPS e.Max, 0.6mm×8.0mm diameter) and disk-shaped composite resin background specimens (4.0mm×8.0mm diameter) were prepared and divided into 10 groups (n=5). These paired specimens were bonded using ten shades of resin cement (Variolink Veneer, shades LV-3, LV-2, MV, HV+2, HV+3; Panavia F, shades light and brown; and RelyX™ Veneer, shades WO, TR, A3). A spectrophotometer (VITA Easyshade) was used to measure the color parameters (CIE Lab* values) of the paired disks before and after cementation. The color differences (ΔE values) after cementation were calculated and statistically analyzed by the One-way ANOVA (at the significant level p<0.05).

RESULTS

The color parameters of the ceramic disks were measured in terms of the increase in L* value, and the decrease in Cab(*) value after bonding with the resin cement. The ΔE values of ceramic disks after cementation ranged from 1.38 to 7.16. The ΔE values were more than 3.3 when the ceramic disks were cemented with resin cements in shade HV+3 (4.90) and shade WO (7.16). One-way ANOVA of ΔE values revealed significant differences in the resin cement shades.

CONCLUSIONS

Resin cements can affect the final color of ceramic veneer restorations, and the extent of this effect varies according to the resin cement shades.