Synthesis of functional xLayMn/KIT-6 and features in hot coal gas desulphurization.

To enhance the stability of sorbents during continuous desulphurization-regeneration cycles, KIT-6 with 3D pore channels was used as a support for the sorbents. A series of mesoporous xLayMn/KIT-6 sorbents with different La/Mn atomic ratios were fabricated using a sol-gel method and their desulphurization properties of hot coal gas were investigated at 700-850 °C. 3La97Mn/KIT-6 performed the best at 800 °C with a breakthrough sulphur capacity of 11.56 g sulphur per 100 g sorbent. The eight successive desulphurization (800 °C)-regeneration (600 °C) cycles revealed that 3La97Mn/KIT-6 with endurable regeneration abilities could retain 80% of the initial sulphur capacity. It indicated a better desulphurization performance compared to pure 3La97Mn and 3La97Mn/MCM-41. The fresh and used xLayMn/KIT-6 sorbents were characterized by means of BET, XRD, HRTEM, XPS and H2-TPR techniques. The XRD patterns and HRTEM images of fresh and used 3La97Mn/KIT-6 verified that the utilization of KIT-6 effectively suppressed the aggregation of Mn2O3 particles and improved the stability of the sorbent.