Oriented bone regenerative capacity of octacalcium phosphate/gelatin composites obtained through two-step crystal preparation method.

The present study was designed to investigate whether composite of coprecipitating octacalcium phosphate and gelatin (C-OCP/Gel) has an effect in repairing critical-sized defect of rat calvaria with oriented regenerative bone if implanted. The materials were prepared through two steps to disperse homogenous and well-elongated OCP toward long axis of the crystals in gelatin (Gel) matrix with the distinct concentration 17-44 wt %: OCP precipitates recovered from the coprecipitated with Gel molecules in aqueous solution (referred to as C-OCP hereafter) were mixed again in fresh aqueous Gel solution with various mixing ratio to form C-OCP/Gel for implantation. C-OCP/Gel disks with 9 mm diameter and 1 mm thickness after the dehydrothermal treatment was implanted in 9 mm diameter rat calvaria critical-sized defect. The histology, the histomorphometry in the regenerated bone and the quantitative analysis of the orientation of collagen with picrosirius red staining were carried out. It was found that C-OCP/Gel is capable of not only inducing sufficiently regenerative bone over 80% of the defect coupled with practically complete material biodegradation but also forming oriented bone significantly in relation to the amount of C-OCP in Gel matrix until 12 weeks after the implantation. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1029-1039, 2017.