[封闭剂与牙釉质的黏附]
[The adhesion of sealants to dental enamel].
作者信息
Fujisawa S
出版信息
Dtsch Zahnarztl Z. 1978 Jun;33(6):388-95.
PMID:275047
Abstract
The test product VM 4 of the Kulzer company, Bad Homburg v.d.H., was tested and compared with the commercial products Nuva Seal, Enamelite, and Palakav. Extracted and sealed teeth were kept in water at 37 degrees C for 67 days and subsequently the adhesive strength between dental surface and sealant was tested in tensile strength tests.
摘要
库尔策公司位于巴特洪堡的测试产品VM 4与商业产品Nuva Seal、Enamelite和Palakav进行了测试和比较。将拔出并密封的牙齿在37摄氏度的水中保存67天，随后在拉伸强度测试中测试牙齿表面与密封剂之间的粘合强度。
相似文献
1
[The adhesion of sealants to dental enamel].[封闭剂与牙釉质的黏附]
Dtsch Zahnarztl Z. 1978 Jun;33(6):388-95.
2
[In vitro studies on the concise enamel bond system, based on the acid etching technic, and its clinical uses].[基于酸蚀技术的简洁牙釉质粘结系统的体外研究及其临床应用]
Zahn Mund Kieferheilkd Zentralbl. 1976;64(7):682-7.
3
[Clinical studies on fissure sealants of the Bis-GMA type].[双甲基丙烯酸缩水甘油酯型窝沟封闭剂的临床研究]
Dtsch Zahnarztl Z. 1975 Aug;30(8):502-7.
4
Effect of sealant viscosity on the penetration of resin into etched human enamel.封闭剂粘度对树脂渗入酸蚀人牙釉质的影响。
Oper Dent. 2000 Jul-Aug;25(4):274-82.
5
[Measures for the testing of the adhesiveness of plastic sealers to dental enamel surfaces].[塑料封闭剂与牙釉质表面粘结性的测试方法]
Dtsch Zahnarztl Z. 1979 Sep;34(9):707-9.
6
Influence of the topical application of fluoride on the in vitro adhesion of fissure sealants.氟化物局部应用对窝沟封闭剂体外黏附的影响。
J Dent Res. 1977 Jan;56(1):17-20. doi: 10.1177/00220345770560010201.
7
[Clinical studies of Nuva Seal, Epoxylite 9070 and Fluor-Protector].[Nuva Seal、Epoxylite 9070和氟保护剂的临床研究]
Dtsch Zahnarztl Z. 1977 Nov;32(11):853-5.
8
Enhanced retention of glass-ionomer sealant by enamel etching: a microleakage and scanning electron microscopic study.通过釉质酸蚀增强玻璃离子封闭剂的保留率：一项微渗漏和扫描电子显微镜研究。
Quintessence Int. 1999 Oct;30(10):712-8.
9
Development of adhesive pit and fissure sealants using a MMA resin initiated by a tri-n-butyl borane derivative.使用由三正丁基硼烷衍生物引发的甲基丙烯酸甲酯树脂开发窝沟封闭剂。
J Biomed Mater Res. 1978 Mar;12(2):149-65. doi: 10.1002/jbm.820120203.
10
[Ultrastructure of conditioned enamel surfaces and their adhesive matrices in dental enamel sealing].[牙釉质封闭中条件性釉质表面及其粘结基质的超微结构]
Dtsch Zahnarztl Z. 1976 Jan;31(1):35-46.
Zotero 插件