Dissolution and separation of non-metallic powder from printed circuit boards by using chloride solvent.

Non-metallic components (NMC) in waste printed circuit boards (WPCBs) are made of the thermosetting epoxy resin and glass fiber, which has been a research concern in the waste recycling area. The recycling of thermosetting epoxy resin is a serious challenge due to their permanent cross-linked structure. An efficient approach to chemical recycling of epoxy resin for resource reutilization was developed in this research. ZnCl/CHCOOH aqueous solution was selected as catalysts system to decompose epoxy resin under a mild reaction condition. The influence of reaction parameters such as reaction temperature, time, liquid-solid ratio and ZnCl amount on the decomposition efficiency of epoxy resin and reaction mechanism were investigated. The physical and chemical properties of NMC, reaction solvent and decomposed products were analyzed using scanning electron microscope(SEM), Fourier transform infrared spectroscopy (FT-IR) and Gas chromatography-mass spectrometry (GC-MS). Results showed that up to 81.85% of epoxy resin could be dissolved by using a temperature of 190 °C during 8 h with a mixture of acetic acid (15 wt%): ZnCl (5 g) 20 mL/g. Incompletely coordinated zinc ions enables the cleavage of CN, CBr and CO bonds in the thermosetting brominated epoxy resin, which was mainly converted to phenol, 2-Bromophenol and 2, 4-Dibromophenol with high resource value. And the functional groups of ethyl acetate and acetic acid maintained chemical structure before and after reaction. This research provided a practical approach to the dissolution and reutilization of NMC in WPCBs.