Surface Characteristics and Adhesion of Veneering Composite Resin to PAEK-Based Substructure Restorative Materials.

PURPOSE

To evaluate and compare the shear bond strength (SBS) of composite veneering material to polyetherketoneketone (PEKK), polyetheretherketone (PEEK), zirconia (YZ), and nickel-chromium alloy (NiCr) substructure restorative materials.

MATERIALS AND METHODS

Forty samples (12 × 2 mm) were prepared from four materials: PEKK, PEEK, zirconia, and NiCr alloy (n = 10). The Vickers hardness was evaluated before preparing the surface for bonding by shot-blasting using 110 μm Al O particles. The surface roughness (Ra) of each sample was determined using a noncontact optical profilometer. The veneering resin was bonded onto each sample following primer application. The prepared samples were then subjected to an SBS test using a universal testing machine at 0.5 mm/min crosshead speed. Failure modes and surface topography following debonding were assessed. The data were statistically analyzed using ANOVA and Tukey's post-hoc comparison test (p < 0.05).  RESULTS: The highest and lowest mean surface roughness was observed in PEEK (3.45 ±0.13 μm) and NiCr (1.87 ±0.07 μm) materials, respectively. A significant difference in roughness values was observed between the materials except for NiCr and YZ (p = 0.547). Concerning SBS, PEEK and NiCr exhibited the highest (16.23 ±0.96 MPa) and lowest (10.1 ±0.63 MPa) values. The mean difference in SBS indicated a statistically significant difference between the material groups (p < 0.01).

CONCLUSIONS

PEKK materials demonstrated significantly lower SBS than PEEK and significantly higher SBS values than conventional zirconia and alloy materials. A positive and significant correlation between mean roughness and SBS was observed, but the causality could be either intrinsic to the material or the roughness.