Glutaraldehyde Crosslinked High Content of Amylose/Polyvinyl Alcohol Blend Films with Potent Tensile Strength and Young's Modulus.

In recent years, with the development of green environmental protection, starch film has become of interest due to the wide availability of sources, low price, and biodegradability. Amylose/polyvinyl alcohol (PVA) blend films crosslinked with different amounts of glutaraldehyde (GLU) were prepared by a solution casting method. The cross-linking degree, water sorption, tensile property, crystallization and section morphology of the films were examined. With the increase in glutaraldehyde concentration, the cross-linking degree of the blend film was improved. The wide-angle X-ray scattering (WAXS) result indicated that cross-linking hindered the crystallization of film. The section morphology of films was examined by scanning electron microscope (SEM). The results showed that the cross-linking degree of amylose film improved while the crystallinity decreased with the increase in glutaraldehyde content. Cross-linking had no obvious effect on the water sorption property of the blend films. The cross-linking modification significantly enhanced the tensile strength and Young's modulus, while it reduced the elongation at break of the blend films. It was found that the film with 0.5 wt % glutaraldehyde possessed the best performance: the tensile strength increased by 115%, while the elongation at break decreased by 18% even at high relative humidity (RH) of 90% compared to non-crosslinked films. The developed amylose/PVA blend films have promising application prospects as agricultural mulch films and packaging materials.