[Flow of molten metal in denture base in horizontal centrifugal casting procedure. (Part 2) Flow, inflow volume and casting time of molten metal passing through several sprues into model denture plate mold (author's transl)].

Two types of spruing methods were used in the casting of the denture type model pattern (thickness, 0.43 mm). Flow of molten metal in the mold was filmed by the improved system of Part 1. When three sprues were attached to the pattern vertically, molten metal passed through each sprue gate flowed being affected by the direction of gravity and revolution of casting machine, and gathered at the lower part of the mold. Next molten metal filled the mold from the lower part to the upper part. In this spruing type, molten metal turned its direction of flow several times. At the middle stage of casting, the inflow volume per unit time (inflow rate), v (mm3/10-2)s)was evaluated as v = 12.36 + 5.16A-0.16 A2 (A: total cross-sectional areas of sprues). The inflow rate increased with increase of the area of the sprues, but it saturated. When the main sprue and the subsprues were attached at the posterior border, the molten metal filled the mold from the lower part to the upper part quietly. In this spruing type, the casting mold was set facing its sprue gates downwards. The inflow rate at the middle stage of casting was evaluated as v = 21.05 + 1.79 C (C: the cross-sectional area of the main sprue). The inflow rate increased linearly with increase of the area of the main sprue.