Evaluation of sunlight stability of polyurethane elastomers for maxillofacial use. II.

The effect of selected UV stabilizers on the stability of mechanical properties of a polyurethane material, Calthane ND2300, was evaluated. The addition of UV stabilizers prolonged the service life of the systems studied but did not achieve completely satisfactory results. The tensile strength and modulus of elasticity decreased after extended exposure to UV. The rate of decrease, however, was much less for the specimens with UV stabilizers. The polyurethane system that contains a mixture of a UV stabilizer and an antioxidant is considered to be the best of the groups tested, in terms of the percentage of retention of tensile strength and modulus of elasticity. It was also found that elongation at break was increased when the duration of UV aging was increased. This phenomenon occurred in all the systems, with or without UV stabilizers, and can be understood in terms of the concepts of the fragmentation of macromolecules that resulted from UV aging. The physical appearance in conjunction with mechanical property tests are needed to ensure the successful performance of any UV stabilizer.