Dentastic bond strength to dentin.

PURPOSE

To evaluate the shear bond strength to the dentin of permanent teeth and failure site of Dentastic hydrophilic dentin bonding agent.

MATERIALS AND METHODS

Forty permanent noncarious molar teeth stored in distilled water were obtained. The teeth were cleaned with pumice and a rubber cup. The mesio-buccal surface of the teeth was ground flat with hand pressure with a series of SiC paper ending with the 600 grit to provide a uniform surface on dentin to which the resin composite could be applied. After preparing the tooth surface, the teeth were stored in distilled water for 48 hours. They were then divided at random into four groups of 10 specimens each: Group 1: Dentastic, five coats of primer; Group 2: Dentastic, three coats of primer; Group 3: Dentastic, five coats of primer, light-cured adhesive before resin bonding; Group 4: Dentastic, three coats of primer, light-cured adhesive before resin bonding. All specimens were thermocycled (500x) and sheared in a testing machine. After shear testing, the debonded sites of all samples were examined with a stereomicroscope and a scanning electron microscope.

RESULTS

The results in MPa were: Group 1: 22.63 +/- 6.24; Group 2: 23.35 +/- 5.14; Group 3: 23.58 +/- 5.66; Group 4: 27.26 +/- 8.22. ANOVA and Student-Newman-Keuls showed no statistically significant difference between the groups. In all groups, all specimens failed at the dentin (dentin cohesive failure = dentin fracture) or at the resin (resin cohesive failure = resin fracture). This means that the bond strength of the product is stronger than the cohesive strengths of the dentin and the resin.