Tamura Jiro, Clarke Ian C, Kawanabe Keiichi, Akagi Masao, Good Victoria D, Williams Paul A, Masaoka Toshinori, Schroeder Dave, Oonishi Hironobu
Peterson Tribology Laboratory, Department of Orthopedic Surgery, Loma Linda University, San Bernardino, California 92408, USA.
J Biomed Mater Res. 2002 Aug;61(2):218-25. doi: 10.1002/jbm.10027.
The objective of this study was to examine both simulator and retrieved total knee replacement polyethylene inserts to confirm, using scanning electron microscopy, whether similar micro-wear patterns to those seen on retrieved inserts were reproduced on simulator specimens. The simulator specimens consisted of samples subjected to sliding and rolling movement (Experiment 1) and to sliding movement only (Experiment 2). Samples from Experiment 1 demonstrated longitudinal patterns in the middle of the wear track and transverse patterns in the anterior and posterior ends, whereas in Experiment 2, only transverse patterns were observed. In the retrieved specimens, both longitudinal and transverse patterns were observed. The results showed that the simulator study reproduced similar patterns of micro-damage on polyethylene, and that the longitudinal micro-wear pattern was related to the rolling movement that is distinctive in knee kinematics.