Solubility of root-canal sealers in water and artificial saliva.

AIM

To compare the weight loss of eight different root-canal sealers in water and in artificial saliva with different pH values.

METHODOLOGY

For standardized samples (n = 12 per group), ring moulds were filled with epoxy resin (AH 26, AH Plus)-, silicone (RSA RoekoSeal)-, calcium hydroxide (Apexit, Sealapex)-, zinc oxide-eugenol (Aptal-Harz)-, glass-ionomer (Ketac Endo)- and polyketone (Diaket)-based sealers. These samples were immersed in double-distilled water or artificial saliva with different pH values (7.0, 5.7 and 4.5) for 30 s, 1 min, 2 min, 5 min, 10 min, 20 min, 1 h, 2 h, 10 h, 24 h, 48 h, 72 h, 14 days and 28 days. Mean loss of weight was determined and analysed statistically using a one-way anova and Student-Newman-Keuls test for all pairwise comparisons.

RESULTS

Most sealers were of low solubility, although Sealapex, Aptal-Harz and Ketac Endo showed a marked weight loss in all liquids. Even after 28 days of storage in water, AH 26, AH Plus, RSA RoekoSeal, and Diaket showed less than 3% weight loss. At exposure times greater than 14 days, Sealapex showed the significantly greatest weight loss of all sealers tested (P < 0.05). Aptal-Harz and Ketac Endo were significantly more soluble in saliva (pH 4.5) than in water (P < 0.05).

CONCLUSIONS

Under the conditions of the present study, AH Plus showed the least weight loss of all sealers tested, independent of the solubility medium used. Sealapex, Aptal-Harz and Ketac Endo had a marked weight loss in all liquids.