Rusnah M, Andanastuti M, Idris B
Bahagian Teknologi Perubatan, Institut Penyelidikan Teknologi Nuklear Malaysia (MINT).
Med J Malaysia. 2004 May;59 Suppl B:83-4.
The paper discusses the influence of sintering temperature on the microstructure and strength of hydroxyapatite ceramics prepared using the extrusion process. The average pore diameters observed were in the range of approximately 150mm to 300mm whereas the compaction strength was found to be around 120-160 MPa.
本文讨论了烧结温度对采用挤压工艺制备的羟基磷灰石陶瓷微观结构和强度的影响。观察到的平均孔径在约150μm至300μm范围内，而压实强度约为120 - 160MPa。