OBJECTIVES

This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue.

METHODS

Forty-two Y-TZP plates (12mm x 12mm x 0.5mm) veneered with pressable porcelain (12mm x 12mm x 1.2mm) and adhesively luted to water aged composite resin blocks (12mm x 12mm x 4mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n=3). Fatigue loading was delivered on specimen either on axial (n=18) or off-axis 30 degrees angulation (n=18) to simulate posterior tooth cusp inclination creating a 0.7mm slide. Single load and fatigue tests utilized a 6.25mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200N (90% CB) were calculated.

RESULTS

The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed.

CONCLUSIONS

Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer.