Effect of five commercial mouth rinses on the microhardness of a nanofilled resin composite restorative material: An in vitro study.

AIM AND OBJECTIVES

This in vitro study was designed to comparatively evaluate the effect of five commercial mouth rinses on the micro hardness of a nanofilled resin based restorative material.

MATERIALS AND METHODS

Fifty specimens of resin composite material (Filtek Z350XT, 3M ESPE, St.Paul, MN USA) were prepared and immersed in artificial saliva for 24 h. The base line micro hardness of specimens was recorded using Vicker's micro hardness tester (MMT - X7 Matsuzawa, Japan). The specimens were randomly distributed into five groups, each containing 10 specimens (n=10) as follows - Group I Listerine (alcohol based), Group II Periogard (alcohol based), Group III Colgate plax (alcohol based), Group IV C- prev (alcohol free), Group V Hiora(alcohol free). The specimens were immersed in 20 ml of mouth rinses and incubated for 24 h at 37°C. The post immersion micro hardness values of the specimens were recorded and the data was tabulated for statistical analysis. Kruskal-Wallis test was used for inter group comparison followed by pair wise comparison of groups using Mann-Whitney U test. The level of significance was set at P=0.05.

RESULTS

Significant reduction in the mean VHN (Vicker's micro hardness number) was observed in all the groups after exposure to the tested mouth rinses (P<0.01) and the reduction in mean VHN values were as follows: Group I 12.09, Group II 3.42, Group II 1.51, Group IV 1.03, Group V 0.57. Inter group comparison showed statistically significant reduction in micro hardness in Groups I and II compared to all other groups with P<0.001. There was no significant difference between Groups III, IV and V.

CONCLUSION

All the mouth rinses showed a reduction in the microhardness of nanofilled resin composite material with listerine (Group I) containing maximum amount of alcohol, showing highest reduction in micro hardness value.