J Am Chem Soc. 2013 Mar 27;135(12):4612-5. doi: 10.1021/ja3122872. Epub 2013 Mar 18.
A Ca(2+) porous coordination polymer with 1D channels was functionalized by the postsynthesis addition of LiCl to enhance the H(+) conductivity. The compound showed over 10(-2) S cm(-1) at 25 °C and 20% relative humidity. Pulse-field gradient NMR elucidated that the fast H(+) conductivity was achieved by the support of Li(+) ion movements in the channel.