Bunte M, Strunz V, Gross U M, Brömer H, Deutscher K
Dtsch Zahnarztl Z. 1977 Oct;32(10):825-8.
After earlier experiments showed that bone became adherent to glass ceramic, the maximum mechanical stress on the bone-ceramic interface, as compared with polymethylmethacrylate (PMMA) and aluminium oxide ceramic, was investigated for shearing force and tension. Whereas the PMMA and aluminium oxide ceramic test objects which had been inclosed in the connective tissue were very easily pushed out without measurable pressure, the average fracture load for 15 smooth glass ceramic objects was 466 p/mm2 in the pushed out test and 167 p/mm2 in the tension test.
早期实验表明骨能附着于玻璃陶瓷后，针对剪切力和拉力，研究了与聚甲基丙烯酸甲酯（PMMA）和氧化铝陶瓷相比，骨 - 陶瓷界面上的最大机械应力。包裹在结缔组织中的PMMA和氧化铝陶瓷测试对象在无明显压力的情况下很容易被推出，而15个光滑玻璃陶瓷对象在推出测试中的平均断裂载荷为466 p/mm²，在拉伸测试中为167 p/mm²。