Reactive Compatibilization of Polyamide 6/Olefin Block Copolymer Blends: Phase Morphology, Rheological Behavior, Thermal Behavior, and Mechanical Properties.

In this study, the morphology, rheological behavior, thermal behavior, and mechanical properties of a polyamide 6 (PA6) and olefin block copolymer (OBC) blend compatibilized with maleic anhydride-grafted polyethylene-octene copolymer (POE-g-MAH) were investigated. The morphological observations showed that the addition of POE-g-MAH enhanced the OBC particle dispersion in the PA6 matrix, suggesting a better interfacial compatibility between the pure PA6 and OBC. The results of the Fourier transform infrared (FTIR) spectroscopy analysis and the Molau test confirmed the compatibilization reactions between POE-g-MAH and PA6. The rheological test revealed that the melt viscosity, storage modulus (G'), and loss modulus (G") of the compatibilized PA6/OBC blends at low frequency were increased with the increasing POE-g-MAH content. The thermal analysis indicated that the addition of OBC had little effect on the crystallization behavior of PA6, while the incorporation of POE-g-MAH at high content (7 wt%) in the PA6/OBC blend restricted the crystallization of PA6. In addition, the compatibilized blends exhibited a significant enhancement in impact strength compared to the uncompatibilized PA6/OBC blend, in which the highest value of impact strength obtained at a POE-g-MAH content of 7 wt% was about 194% higher than that of pure PA6 under our experimental conditions.