Effect of different surface treatments on the biaxial flexure strength, Weibull characteristics, roughness, and surface topography of bonded CAD/CAM silica-based ceramics.

OBJECTIVE

To investigate the influence of different surface treatments on biaxial flexure strength, roughness, and surface topography of lithium silicate/disilicate-based ceramics.

METHODS

225 discs (∅: 12 mm; 1.2 mm - ISO 6872) were made from three ceramics: IPS e.max CAD (LD - Ivoclar Vivadent), Suprinity (LSS - Vita) and Celtra Duo (LSC - Dentsply). The samples were randomly divided into 5 groups (n = 15): no treatment (C); 10% hydrofluoric acid + silane (HF); sandblasting AlO + silane (SB); silicatization + silane (SC); and self-etching ceramic primer (SEP). After surface treatment, a resin cement layer was applied to the disc surface (RelyX U200, 3M ESPE), mechanical cycled (1.2 × 10 cycles, 50 N, 3.8 Hz) and submitted to biaxial flexural strength test (1 mm/min, 1000 Kgf). Roughness, EDS and SEM were also performed. Data were analyzed by one-way ANOVA, Tukey test (5%) and Weibull.

RESULTS

ANOVA revealed that the "surface treatment" factor was significant for all ceramics (p < 0.05). The groups LD-HF (289.30 ± 40) LD-SEP (298. 87 ± 53.29), LSC-HF (195.51 ± 42.12), LSS-HF (269.58 ± 27.07) and LSS-SEP (207.45 ± 28.63) presented significantly higher biaxial flexure strength than respective control groups, except for the LSC-SEP (165.41 ± 33.86), which was statistically similar to the control. The Weibull modulus was significantly higher for the LD-SB, LSC-SC groups. Additionally, the LD-SB, LSC-SC and LSS-HF groups showed higher roughness compared to the other treatments.

SIGNIFICANCE

HF etching followed by silanization and self-etching ceramic primer are the most suitable surface treatments for lithium silicate/disilicate-based glass-ceramics.