[Studies of dental methacrylic resin. (Part 8) Flexural and impact adhesive strength of self-curing methacrylic resin to cross-linked polymethyl methacrylate resins (author's transl)].

Heat-curing methacylic resins cross-linked with three kinds of dimethacrylates, i.e. EDMA, tri-EDMA and nona-EDMA, were prepared, and the flexural and the impact adhesive strength of the dough moulding type and the pour type self-curing methacrylic resins to them were examined. The results obtained were as follows. (1) The flexural and the impact adhesive strength of the pour type self-curing resin were higher and more stable than those of the dough moulding type one. (2) The flexural and the impact adhesive strength of self-curing resins to cross-linked adherent resins rised in order of nona-EDMA greater than tri-EDMA greater than EDMA in the range of higher concentration of cross-linking agents. This tendency was marked for the pour type resin. (3) When the dough moulding type resin was used as adhesive resin, to adherent resin cross-linked with EDMA or tri-EDMA which had relatively short chain, the respective adhesive strength of that decreased with increasing the concentration of cross-linking agent. While, to adherent resin cross-linked with nona-EDMA, which had relatively long and more flexible chain, the respective adhesive strength of the dough moulding type resin increased with increasing the concentration of cross-linking agent. (4) When the pour type resin was used as adhesive resin, to adherent resin cross-linked with EDMA or tri-EDMA, the respective adhesive strength of that showed the maximum at the concentration near 2 to 5 mole% and decreased with increasing the concentration. While, to adherent resin cross-linked with nona-EDMA, the flexural adhesive strength of the pour type resin was approximately constant without the effect of the concentration, but the impact adhesive strength of that increased with increasing the concentration. (5) The flexural adhesive strength of the dough moulding and the pour type resin under the wet condition decreased about 30 to 60% compared with under the dry condition, but the percentage of the falling for the impact adhesive strength was about 15 to 30% and relatively small. (6) The flexural adhesive strength showed a similar adhesive tendency to the tensile adhesive strength, but the impact adhesive strength showed a different adhesive tendency from those.