Sung H W, Tu R, Shen S H, Witzel T H, Lin D, Hata C, Kingsbury C J, Noishiki Y, Tomizawa Y, Quijano R C
Department of Chemical Engineering, National Center University, Taoyuan, Taiwan, Republic of China.
ASAIO J. 1994 Apr-Jun;40(2):192-8.
Concerns with currently available bioprostheses are calcification, long-term durability, and functional and hemodynamic performance. It has been well known that these concerns are all more or less related to the fixatives, glutaraldehyde or formaldehyde, used in preserving bioprostheses. To address these concerns, we undertook the development of a porcine bioprosthesis fixed with an epoxy compound. It was discovered that the porcine leaflets fixed with the epoxy compound appeared more natural than those preserved with glutaraldehyde. The performance of this newly developed epoxy compound bioprosthesis (three samples) was evaluated in a juvenile sheep model. The results were compared to those of its glutaraldehyde counterpart (three samples). Two-dimensional echocardiographic inspection of the valvular leaflet motion indicated that the epoxy compound leaflets were more pliable than their glutaraldehyde counterparts. In addition, the epoxy compound valve appeared to open more widely than the glutaraldehyde valve. Color Doppler flow mapping demonstrated that the blood flow distal to the epoxy compound valve was slightly broader than that observed distal to the glutaraldehyde valve. Moreover, at retrieval, less calcium and pannus ingrowth were observed in the epoxy compound valve than its glutaraldehyde counterpart. The results of this preliminary evaluation indicated that the performance of this newly developed epoxy compound valve was at least equivalent to its glutaraldehyde counterpart, if not better.