Triolo P T, Swift E J, Barkmeier W W
Operative Dentistry, Creighton University School of Dentistry, Omaha, NE 68178, USA.
Oper Dent. 1995 Mar-Apr;20(2):46-50.
The development of adhesive agents for bonding composite to dentin has rapidly evolved in recent years. It is postulated that dentin bond strengths in the range of 17 MPa are sufficient to resist the polymerization shrinkage of composite resins. The purpose of this study was to evaluate the shear bond strengths of the following dentin adhesive systems: All-Bond 2 (Bisco), Imperva Bond (Shofu), Optibond (Kerr), Permagen (Ultradent), ProBond (Caulk/Dentsply), and Scotchbond Multi-Purpose (3M). Sixty human molars (10 per group) were mounted in phenolic rings, and the occlusal surfaces were flat ground in dentin to 600 grit. The prepared dentin bonding sites were treated according to the directions for each of the systems evaluated. A gelatin capsule technique was used to bond Bis-Fil composite cylinders to the teeth. The specimens were stored in water at 37 degrees C for 24 hours. Mean shear bond strengths were as follows: Scotchbond Multi-Purpose: 23.1 +/- 2.6 MPa, All-Bond 2: 21.4 +/- 7.8 MPa, Imperva Bond: 19.8 +/- 6.1 MPa, Optibond: 19.7 +/- 3.6 MPa, ProBond: 16.3 +/- 4.5 MPa, and Permagen: 16.2 +/- 3.0 MPa. There was not a significant difference (P<0.05) in the bond strengths of Scotchbond Multi-Purpose, All-Bond 2, Imperva Bond, and Optibond. The bond strengths of Scotchbond Multi-Purpose and All-Bond 2 were significantly greater (P<0.05) than ProBond and Permagen. Current-generation dentin adhesive systems have approached or exceeded the theoretical threshold value to resist contraction stresses during polymerization of resin materials.