Zhang G, Latour R A, Kennedy J M, Del Schutte H, Friedman R J
Department of Bioengineering, Clemson University, SC 29634, USA.
Biomaterials. 1996 Apr;17(8):781-9. doi: 10.1016/0142-9612(96)81415-3.
In total hip arthroplasty, concerns such as corrosion and stress shielding associated with stiff metallic femoral components have led to the development of low stiffness advanced fibre-reinforced polymer (FRP) composite femoral components. Carbon fibre-reinforced polyetheretherketone (CF/PEEK) composite material is now one of the primary material systems being considered for composite hip stem development. As a hip stem, a composite material must be able to support a complex state of stress in the in vivo environment without failure. Considering the loading conditions of a hip stem (superimposed compression and bending), and the fact that FRP composites typically possess lower compressive than tensile strength, the compressive behaviour of FRP composites becomes very important for femoral component design. This paper presents an investigation of the long-term durability of 0 degree and 90 degrees compressive strengths of CF/PEEK composite following physiological saline saturation. 0 degree and 90 degrees compressive moduli and Poisson ratio (v12) properties are also reported. Samples were tested following conditioning in physiological saline at 37, 65 and 95 degrees C for time periods from 0 to 5000 h. Dry samples were tested as controls. Results show no significant loss in compressive property values of the saline-saturated or the dry control samples as a function of conditioning time or temperature.