Yun Y H, Turitto V T, Daigle K P, Kovacs P, Davidson J A, Slack S M
Department of Biomedical Engineering, University of Memphis, TN 38152, USA.
J Biomed Mater Res. 1996 Sep;32(1):77-85. doi: 10.1002/(SICI)1097-4636(199609)32:1<77::AID-JBM9>3.0.CO;2-M.
Two novel metal alloys, Ti-13Nb-13Zr and Zr-2.5Nb, have been engineered for applications in orthopedic implants because of their favorable mechanical properties, corrosion resistance, and compatibility with bone and tissue. These alloys also have the ability to form a hard, abrasion-resistant, ceramic surface layer upon oxidative heat treatment (diffusion hardening, DH). Previous studies have indicated that these and other ceramics cause limited hemolysis and exhibit remarkable structural integrity after extended exposure to physiological environments. Such observations suggest that DH Ti-13Nb-13Zr and ZrO2/Zr-2.5Nb could be used successfully as components in blood-contacting devices. Materials intended for such applications must possess properties that do not elicit adverse physiological responses, such as the initiation of the coagulation cascade or thrombus formation. In the present study measurements of prekallikrein activation, fibrinogen adsorption from diluted human plasma, and the strength of fibrinogen attachment as judged by residence-time experiments were performed to evaluate the potential hemocompatibility of these materials. The results of the prekallikrein activation and fibrinogen-retention studies correlated well with two electrochemical properties of the alloys, the open circuit potential and reciprocal polarization resistance. The results indicate that both the original and treated Ti and Zr alloys activate prekallikrein and adsorb as well as retain fibrinogen in amounts similar to other materials used as components of blood-contacting devices. On the basis of these studies, these alloys appear to be promising candidates for cardiovascular applications and merit further investigation.