采用接触膜转移法制备双层双极性有机薄膜晶体管和逆变器。
Bilayer ambipolar organic thin-film transistors and inverters prepared by the contact-film-transfer method.
机构信息
Department of Applied Chemistry, School of Engineering, The University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-8656, Japan.
出版信息
ACS Appl Mater Interfaces. 2009 Sep;1(9):1865-8. doi: 10.1021/am9004545.
Ambipolar organic thin-film transistors with a bilayer structure of poly(3-hexylthiophene) and [6,6]phenyl C(61) butyric acid methyl ester were fabricated using a simple solution-based, contact-film-transfer method. The transistors exhibited balanced electron and hole mobilities of 2.1 x 10(-2) and 1.1 x 10(-2) cm(2) V(-1) s(-1), respectively. Complementary inverters based on two identical ambipolar transistors showed good performance with a gain of 14.
采用简单的溶液基底接触膜转移方法制备了具有聚（3-己基噻吩）和[6,6]-苯基 C（61）丁酸甲酯双层结构的双极有机薄膜晶体管。晶体管表现出平衡的电子和空穴迁移率，分别为 2.1×10（-2）和 1.1×10（-2）cm（2）V（-1）s（-1）。基于两个相同的双极晶体管的互补反相器表现出良好的性能，增益为 14。