Magnetic and Cytotoxicity Properties of La(1-x)Sr(x)MnO(3) (0 </= x </= 0.5) Nanoparticles Prepared by a Simple Thermal Hydro-Decomposition.

This study reports the magnetic and cytotoxicity properties of magnetic nanoparticles of La(1-x)Sr(x)MnO(3) (LSMO) with x = 0, 0.1, 0.2, 0.3, 0.4, and 0.5 by a simple thermal decomposition method by using acetate salts of La, Sr, and Mn as starting materials in aqueous solution. To obtain the LSMO nanoparticles, thermal decomposition of the precursor was carried out at the temperatures of 600, 700, 800, and 900 degrees C for 6 h. The synthesized LSMO nanoparticles were characterized by XRD, FT-IR, TEM, and SEM. Structural characterization shows that the prepared particles consist of two phases of LaMnO(3) (LMO) and LSMO with crystallite sizes ranging from 20 nm to 87 nm. All the prepared samples have a perovskite structure with transformation from cubic to rhombohedral at thermal decomposition temperature higher than 900 degrees C in LSMO samples of x </= 0.3. Basic magnetic characteristics such as saturated magnetization (M(S)) and coercive field (H(C)) were evaluated by vibrating sample magnetometry at room temperature (20 degrees C). The samples show paramagnetic behavior for all the samples with x = 0 or LMO, and a superparamagnetic behavior for the other samples having M(S) values of ~20-47 emu/g and the H(C) values of ~10-40 Oe, depending on the crystallite size and thermal decomposition temperature. Cytotoxicity of the synthesized LSMO nanoparticles was also evaluated with NIH 3T3 cells and the result shows that the synthesized nanoparticles were not toxic to the cells as determined from cell viability in response to the liquid extract of LSMO nanoparticles.