Mohamed R M, Mkhalid I A, Al-Thabaiti S A, Mokhtar Mohamed
Faculty of Science, Chemistry Department, King Abdulaziz University, PO Box: 80203, Jeddah 21589, Saudi Arabia.
J Nanosci Nanotechnol. 2013 Jul;13(7):4975-80. doi: 10.1166/jnn.2013.7602.
The photo-assisted deposition (PAD) and impregnation (Img) synthesis of nano-sized Cu metal on TiO2-SiO2 are reported. The prepared catalysts were characterized by different techniques such as XRD, EXAFS, TEM and nitrogen adsorption analysis. Photocatalytic reactivity using Cu-TiO2-SiO2 catalysts under visible-light condition on the oxidation of direct blue dye with O2 reaction was evaluated. The results have shown notable photocatalytic activity of PAD-Cu/TiO2-SiO2 which was 1.6 and 10 times higher than that of Img-Cu/TiO2-SiO2 and TiO2-SiO2, respectively.