Lutz F, McDermott T, Lüscher B, Mühlemann H R
SSO Schweiz Monatsschr Zahnheilkd. 1978 May;88(5):603-12.
The marginal integrity of MOD adhesive restorations of a thixotropic test composite (ZKP-A-5) and of two injection-capsule composites (Concise -capsule composite and Compocap-S) was examined. Dy penetration tests measured microleakage and scanning electron microscope evaluated marginal adaptation. The test restorations showed no improved micromorphological marginal adaptation when compared to those of a standard paste-paste composite (Concise). Compocap-S demonstrated better prevention of microleakage than did the other test preparations. The marginal quality of these thixotropic and injection-capsule composite restorations was improved from 34% to 52% with utilization of a sealer application (ZKP-A-2), (Concise-Enamel Bond). The application of a sealer prior to insertion of thixotropic and injection-capsule composites is, therefore, definitely indicated when these materials are used. The resultant restorations obtained with these test materials plus sealer correspond qualitatively to those of standard composites Concise or Adaptic [6,7]. The newly developed, complete composite systems (Nimetic, GC's Epolite 100/Epobond) demonstrated in comparison to Concise and Adaptic [6,7] inferior results.
对一种触变测试复合材料（ZKP-A-5）以及两种注射胶囊复合材料（Concise胶囊复合材料和Compocap-S）的MOD粘结修复体的边缘完整性进行了检查。染料渗透测试测量微渗漏情况，扫描电子显微镜评估边缘适应性。与标准膏体-膏体复合材料（Concise）相比，测试修复体在微观形态边缘适应性方面没有改善。Compocap-S在预防微渗漏方面比其他测试制剂表现更好。使用封闭剂（ZKP-A-2，Concise-Enamel Bond）后，这些触变和注射胶囊复合材料修复体的边缘质量从34%提高到了52%。因此，当使用这些材料时，在插入触变和注射胶囊复合材料之前应用封闭剂是明确必要的。使用这些测试材料加封闭剂所得到的修复体在质量上与标准复合材料Concise或Adaptic相当[6,7]。与Concise和Adaptic[6,7]相比，新开发的完整复合系统（Nimetic，GC的Epolite 100/Epobond）显示出较差的结果。