Push-out Bond Strength of Fast-setting Mineral Trioxide Aggregate and Pozzolan-based Cements: ENDOCEM MTA and ENDOCEM Zr.

机构信息

Department of Endodontics, School of Dentistry, Grande Rio University, Rio de Janeiro, Rio de Janeiro, Brazil.

Department of Endodontics, Rio de Janeiro State University, Rio de Janeiro, Rio de Janeiro, Brazil.

出版信息

J Endod. 2017 May;43(5):801-804. doi: 10.1016/j.joen.2016.12.007. Epub 2017 Mar 11.

DOI:10.1016/j.joen.2016.12.007

PMID:28292603

Abstract

INTRODUCTION

The present study investigated the root canal dentin bond strength of 2 newly developed fast-setting mineral trioxide aggregate (MTA) and pozzolan-based cements: ENDOCEM MTA (Maruchi, Wonju, Korea) and ENDOCEM Zr (Maruchi). White MTA (Angelus, Londrina, Brazil) was used as the reference material for comparison.

METHODS

Root slices (1 mm ± 0.1 mm) were obtained from the middle third of 15 maxillary incisors previously selected. Three canal-like holes (0.8 diameter) were drilled perpendicularly on the axial surface of each root slice. A standardized irrigation protocol was applied for all samples, and after drying, each hole was filled with 1 of 3 test repair materials. Finally, slices were stored in contact with phosphate-buffered saline solution (pH = 7.2) for 7 days at 37°C before the push-out assay. Data were nonparametrically evaluated at α = 5%.

RESULTS

The Friedman test was unable to confirm a significant dissimilarity in push-out ranks among the tested cements (P = .220).

CONCLUSIONS

The new fast-setting MTA and pozzolan-based cements ENDOCEM MTA and ENDOCEM Zr present suitable bond strength performance, which is comparable with white MTA.