Polymethylmethacrylate Incorporating Nanodiamonds for Denture Repair: In Vitro Study on the Mechanical Properties.

OBJECTIVE

This study aimed to evaluate the effect of nanodiamond (ND) addition to repair resin with repair gap modifications on the flexural and impact strength of repaired polymethylmethacrylate denture base.

MATERIALS AND METHODS

Heat-polymerized acrylic resin specimens ( = 100/test) were prepared and sectioned to half creating two repair gaps: 2.5- and 0 mm with 45 degrees beveling. They were further divided into subgroups ( = 20) according to ND concentration (control, 0.25%ND, and 0.50%ND), thermocycling (500 cycles) was done to half the specimens in each subgroup. Flexural strength was tested using 3-point bending test and impact strength was tested by Charpy's impact test. Analysis of variance and post-hoc Tukey's tests were performed for data analysis ( = 0.05). Scanning electron microscope was employed for fracture surface analysis and ND distribution.

RESULTS

Before and after thermocycling, the addition of ND significantly increased the flexural strength and elastic modulus in comparison to control group ( ˂ 0.001), while 0 mm repair gap showed insignificant difference between ND-reinforced groups ( ˃ 0.05). Regarding impact strength, ND addition increased the impact strength with 0 mm gap in comparison to control and 2.5 mm with ND (˂0.001), while later groups showed no significant in between ( ˃ 0.05). Comparing thermocycling effect per respective concentration and repair gap, thermocycling adversely affected all tested properties except elastic modulus with 0 mm-0.25 and 0 mm-0.5% and impact strength with 2.5 mm, 2.5 mm-0.25%, 2.5 mm- 0.5% ( ˃ 0.05).

CONCLUSION

ND addition combined with decreased repair gap improved the flexural strength, elastic modulus, and impact strength of repaired denture resin, while thermocycling has a negative effect on denture repair strength.