Effect of Various Acid Solutions as an Aid in Removing the OrthoMTA-Based Root Canal Filling.

UNLABELLED

The objectives of this study were to compare the effects of various acid solutions combined with ultrasonics as an aid to remove mineral trioxide aggregate (MTA)-based root canal filling and to assess their effect on the surface topography and microhardness of root canal dentin.

MATERIALS AND METHOD

Fifty human permanent single rooted and single canaled freshly extracted teeth were decoronated and sectioned apically to prepare the middle third of root sections of 5 mm length. The canals were prepared in a step-back manner. OrthoMTA was packed throughout the prepared canals. These root sections were incubated for one week and subsequently randomly allocated to five groups (n = 10) according to the OrthoMTA removal method: No treatment (NT); 5% glycolic acid + ultrasonics (5% GA+U); 10% glycolic acid + ultrasonics (10% GA+U); 10% citric acid + ultrasonics (10% CA+U); Distilled water + ultrasonics (DW+U). A 1 mm deep well was created within the coronal end of the set OrthoMTA. Wells were filled with each respective test solution and left for 5 min. Thereafter, further removal of OrthoMTA used a specific ultrasonic tip. Finally, the canals were flushed using 1 mL of the respective test solutions and activated with a Controlled Memory ultrasonic tip for two cycles of 20 s each followed by flushing with 1 mL of distilled water and paper point drying of the canals. Then, specimens were longitudinally split into two halves and examined under a scanning electron microscope (1000×) to assess the residual OrthoMTA and surface topography of root canal dentin. The Vickers surface microhardness of treated radicular dentin was measured using the HMV-2 microhardness tester.

RESULT

Data were analysed using one-way ANOVA followed by Tukey's post hoc test. Significant differences for residual OrthoMTA were observed between (10% GA+U) with (5% GA+U), (10% CA+U), (DW+U) and (NT) ( value < 0.01). In the context of microhardness, (5% GA+U) and (10% GA+U) showed statistically significant difference compared to (NT), (10% CA+U) and (DW+U) ( value < 0.01).

CONCLUSION

10% GA+U was superior to other tested groups in removing OrthoMTA, but it substantially reduced dentin microhardness.