Influence of argon laser curing on resin bond strength.

Light cured resin composites are usually cured with halogen lamps whose light output decreases with time and distance to the resin surface. This study compared bond strengths of resins to tooth structure cured with either an argon laser or a conventional halogen light. The enamel and dentin of bovine incisors were ground on the buccal surface with wet #600 grit SiC paper. A 4 x 2 mm mold was placed on the tooth surface and Scotchbond 2/Silux and Clearfil Photobond/Photo Clearfil A were placed into the molds and cured using a Quick Light or an argon laser for exposure times of 10, 20, and 30 seconds, and distances of 0.0, 0.5, 1.0, and 1.5 mm from the resin surface. The intensity of the Quick Light was measured as 510 mW/cm2 at 470 +/- 15 nm and the intensity of the argon laser was adjusted to 510 mW/cm2 before curing. Shear bond tests at a crosshead speed of 1.0 mm/min were performed after 24 hours of storage in water. The bond strengths obtained with the halogen lamp and the laser were not significantly different at the same exposure times and at 0.0 or 0.5 mm from the resin surface. The laser cured bond strengths did not decrease with increasing distance whereas there was a significant decrease in halogen bond strengths at distances greater than 0.5 mm for both resins. The use of the laser might provide a clinical advantage in cases where the curing light source cannot be brought into proximity to the surface of the resin.