In Vitro Evaluation of Physical and Mechanical Properties of Light-Curing Resin Cement: A Comparative Study.

OBJECTIVE

The aim of study was to evaluate the surface hardness, sorption, solubility, and color stability of three light-cured resin cements, namely RelyX Veneer (RLX), Variolink Veneer (VLK), and All Cem Veneer (ACV).

MATERIALS AND METHODS

Cylindrical samples (15 × 1 mm) were made for each group using a metallic mold ( = 10). Vickers microhardness test was performed, and average hardness was calculated from three indentations (300 gf/15s) per sample. The sorption and solubility of the materials were evaluated according to ISO 4049:2009 based on three samples weighing: initial ( ), after immersion in distilled water for 7 days ( ), and final (after removal of all moisture [ ]). The color change was observed using a digital spectrophotometer, at three different time points, baseline, 1 day, and 1 week of immersion in coffee and distilled water (control).

STATISTICAL ANALYSIS

Shapiro-Wilk test was used to analyze the normality of the data, and groups were compared using Kruskal-Wallis and Mann-Whitney tests. A significance level of 5% was used.

RESULTS

RLX showed the highest microhardness mean values (36.96 VHN), but higher sorption (23.2 µg/mm) and solubility (2.40 µg/mm), with statistically significant differences with the other groups. For color stability, higher ∆E was observed for the samples immersed in coffee ( = 0.009). The VLK resin cement presented statistically significant differences from the other groups, with higher color changes in coffee at 1 day (15.14) and after 1 week (23.65).

CONCLUSION

RLX resin cement showed better hardness results. All materials tested performed satisfactorily for sorption and solubility according to ISO 4049:2009. All materials showed high-staining values after 1 week of immersion in coffee.