Surface changes induced by fluoride prophylactic agents on titanium-based orthodontic wires.

This study investigated the effect of fluoride prophylactic agents on the surfaces of titanium-based orthodontic wires. Four types of titanium-based orthodontic wires (2 nickel-titanium alloy wires [nickel-titanium and copper-nickel-titanium] and 2 beta-titanium alloy wires [titanium-molybdenum and titanium-niobium], all from Ormco, Glendora, Calif) with similar sizes were prepared and immersed in 5 fluoride prophylactic agents (2 acidulated phosphate fluoride agents [Nupro APF (Dentsply International, York, Pa) and Florentine III (Confi-Dental, Louisville, Colo)], 1 neutral agent [Neupro Neutral (Dentsply International)] and 2 stannous fluoride agents [Florentine II (Confi-Dental) and Perio-Med (Omni International, Warrenton, Va)]) for 5 minutes, 1 hour, and 24 hours. After immersion, average surface roughness and color changes were evaluated. The surface changes were observed with a scanning electron microscope. The average surface roughness data were statistically analyzed by analysis of variance and Tukey post hoc test at a significance level of alpha = 0.05. There were no significant differences in average surface roughness value among fluoride solutions or orthodontic wires, except for the titanium-molybdenum wire, which showed significantly (P <.05) higher average surface roughness values after immersion in Nupro APF for 24 hours. The results suggested that a few applications of acidulated phosphate fluoride agents might change the surface color of the beta-titanium alloy wires, particularly the titanium-molybdenum wire, which contains a large amount (about 80%) of titanium.