Wound healing properties of PVA/starch/chitosan hydrogel membranes with nano Zinc oxide as antibacterial wound dressing material.

In this work, hydrogel membranes were developed based on poly vinyl alcohol (PVA), starch (St), and chitosan (Cs) hydrogels with nano Zinc oxide (nZnO). PVA/St/Cs/nZnO hydrogel membranes were prepared by freezing-thawing cycles, and the aqueous PVA/St solutions were prepared by dissolving PVA in distilled water. After the dissolution of PVA, starch was mixed, and the mixture was stirred. Then, chitosan powder was added into acetic acid, and the mixture was stirred to form a chitosan solution. Subsequently, Cs, St and PVA solutions were blended together to form a homogeneous PVA/St/Cs ternary blend solution. Measurement of Equilibrium Swelling Ratio (ESR), Water Vapor Transmission Test (WVTR), mechanical properties, scanning electron microscopy (SEM), MTT [3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyl tetrazolium bromide] assay, antibacterial studies, in vivo wound healing effect and histopathology of the hydrogel membranes were then performed. The examination revealed that the hydrogel membranes were more effective as a wound dressing in the early stages of wound healing and that the gel could be used in topic applications requiring a large spectrum of antibacterial activity; namely, as a bandage for wound dressing.