Structure, optoelectronic properties and thermal stability of the triple organic cation GAFAMAPbI system prepared by mechanochemical synthesis.

Halide perovskites are a well-known class of materials with many interesting applications. Great attention has been devoted to investigating halide perovskites containing triple methylammonium (MA), formamidinium (FA), and guanidinium (GA) cations. Despite presenting very good applied perspectives so far, the lack of fundamental information for this system, such as its structural, thermal, and optoelectronic characteristics, prompts a step back before any technological leap forward. In the present work, we investigate the physical properties of mechanochemically solvent-free synthesized GAFAMAPbI halide perovskite powders with compositions of 0.00 ≤ ≤ 0.15. We demonstrate that the synthesis of the powders can be performed by a simple manual mechanical grinding of the precursors for about 40 minutes, leading to solid solutions with an only minor content of unreacted precursors. X-ray diffraction, differential scanning calorimetry, and infrared spectroscopy techniques were used to investigate the structure, tetragonal-to-cubic phase transition, and vibrational characteristics of the organic cations with increasing GA and FA contents, respectively. The band gap and Urbach energies, obtained from ultraviolet-visible spectroscopy analyses, ranged from 1.58 to 1.65 eV and 23 to 36 meV, respectively, depending on the composition. These parameters demonstrate a non-random variation with composition, which offers the possibility of a rational composition design for a given set of desired properties, demonstrating potential for optoelectronic applications. Finally, the system appears to have adequately tolerated heating for 12 hours at 120 °C in an ambient atmosphere, indicating high thermal stability and low ionic conductivity, which are desirable characteristics for solar cell applications.